| 1. Identificação | ||||
| Tipo de Referência | Artigo em Revista Científica (Journal Article) | |||
| Site | mtc-m21b.sid.inpe.br | |||
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S | |||
| Identificador | 8JMKD3MGP3W34P/3M37572 | |||
| Repositório | sid.inpe.br/mtc-m21b/2016/07.07.18.45 (acesso restrito) | |||
| Última Atualização | 2016:07.07.18.49.48 (UTC) simone | |||
| Repositório de Metadados | sid.inpe.br/mtc-m21b/2016/07.07.18.45.08 | |||
| Última Atualização dos Metadados | 2018:06.04.02.40.59 (UTC) administrator | |||
| DOI | 10.1016/j.dental.2016.03.018 | |||
| ISSN | 0109-5641 1879-0097 | |||
| Chave de Citação | RamosCaLaMaBoCeMe:2016:MiChSC | |||
| Título | Microstructure characterization and SCG of newly engineered dental ceramics  | |||
| Ano | 2016 | |||
| Mês | July | |||
| Data de Acesso | 09 maio 2024 | |||
| Tipo de Trabalho | journal article | |||
| Tipo Secundário | PRE PI | |||
| Número de Arquivos | 1 | |||
| Tamanho | 4434 KiB | |||
| 2. Contextualização | ||||
| Autor | 1 Ramos, Nathália de Carvalho 2 Campos, Tiago Moreira Bastos 3 La Paz, Igor Siqueira de 4 Machado, João Paulo Barros 5 Bottino, Marco Antonio 6 Cesar, Paulo Francisco 7 Melo, Renata Marques de | |||
| Identificador de Curriculo | 1 2 3 4 8JMKD3MGP5W/3C9JHER | |||
| Grupo | 1 2 3 4 LAS-CTE-INPE-MCTI-GOV-BR | |||
| Afiliação | 1 Universidade Estadual Paulista (UNESP) 2 Instituto Tecnológico de Aeronáutica (ITA) 3 Universidade Estadual Paulista (UNESP) 4 Instituto Nacional de Pesquisas Espaciais (INPE) 5 Universidade Estadual Paulista (UNESP) 6 Universidade de São Paulo (USP) 7 Universidade Estadual Paulista (UNESP) | |||
| Endereço de e-Mail do Autor | 1 2 3 4 joao.machado@inpe.br 5 6 7 renata.marinho@ict.unesp.br | |||
| Revista | Dental Materials | |||
| Volume | 32 | |||
| Número | 7 | |||
| Páginas | 870-878 | |||
| Nota Secundária | A1_ODONTOLOGIA A1_INTERDISCIPLINAR A1_ENGENHARIAS_III A1_BIODIVERSIDADE A2_QUÍMICA A2_MEDICINA_II A2_MATERIAIS A2_FARMÁCIA A2_ENGENHARIAS_II A2_CIÊNCIAS_BIOLÓGICAS_I B1_NUTRIÇÃO B1_MATEMÁTICA_/_PROBABILIDADE_E_ESTATÍSTICA B1_ENGENHARIAS_IV B1_CIÊNCIAS_BIOLÓGICAS_II B1_BIOTECNOLOGIA B1_ASTRONOMIA_/_FÍSICA | |||
| Histórico (UTC) | 2016-07-07 18:49:48 :: simone -> administrator :: 2016 2018-06-04 02:40:59 :: administrator -> simone :: 2016 | |||
| 3. Conteúdo e estrutura | ||||
| É a matriz ou uma cópia? | é a matriz | |||
| Estágio do Conteúdo | concluido | |||
| Transferível | 1 | |||
| Tipo do Conteúdo | External Contribution | |||
| Tipo de Versão | publisher | |||
| Palavras-Chave | Ceramics Dental porcelain Glass ceramics Subcritical crack growth Stress corrosion Computer-aided design Flexural strength Young's modulus Spectroscopy | |||
| Resumo | Objectives. The aim of this study was to characterize the microstructure of four dental CAD-CAM ceramics and evaluate their susceptibility to stress corrosion. Methods. SEM and EDS were performed for microstructural characterization. For evaluation of the pattern of crystallization of the ceramics and the molecular composition, XRD and FTIR, respectively, were used. Elastic modulus, Poisson's ratio, density and fracture toughness were also measured. The specimens were subjected to biaxial flexure under five stress rates (0.006, 0.06, 0.6, 6 and 60 MPa/s) to determine the subcritical crack growth parameters (n and D). Twenty-five specimens were further tested in mineral oil for determination of Weibull parameters. Two hundred forty ceramic discs (12 mm diameter and 1.2 mm thick) were made from four ceramics: feldspathic ceramic FEL (Vita Mark II, Vita Zahnfabrik), ceramic-infiltrated polymer PIC (Vita Enamic, Vita Zahnfabrik), lithium disilicate LD (IPS e.max CAD, Ivoclar Vivadent) and zirconia-reinforced lithium silicate LS (Vita Suprinity, Vita Zahnfabrik). Results. PIC discs presented organic and inorganic phases (n = 29.1 +/- 7.7) and Weibull modulus (m) of 8.96. The FEL discs showed n = 36.6 +/- 6.8 and m = 8.02. The LD discs showed a structure with needle-like disilicate grains in a glassy matrix and had the lowest value of n (8.4 +/- 0.8) and m = 6.19. The ZLS discs showed similar rod-like grains, n =11.2 +/- 1.4 and m = 9.98. Significance. The FEL and PIC discs showed the lowest susceptibility to slow crack growth (SCG), whereas the LD and ZLS discs presented the highest. PIC presented the lowest elastic modulus and no crystals in its composition, while ZLS presented tetragonal zirconia. The overall strength and SCG of the new materials did not benefit from the additional phase or microconstituents present in them. | |||
| Área | FISMAT | |||
| Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAS > Microstructure characterization and... | |||
| Conteúdo da Pasta doc | acessar | |||
| Conteúdo da Pasta source | não têm arquivos | |||
| Conteúdo da Pasta agreement |
| |||
| 4. Condições de acesso e uso | ||||
| Idioma | en | |||
| Arquivo Alvo | ramos_microsctructure.pdf | |||
| Grupo de Usuários | simone | |||
| Grupo de Leitores | administrator simone | |||
| Visibilidade | shown | |||
| Permissão de Leitura | deny from all and allow from 150.163 | |||
| Permissão de Atualização | não transferida | |||
| 5. Fontes relacionadas | ||||
| Repositório Espelho | urlib.net/www/2011/03.29.20.55 | |||
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ESR3H2 | |||
| Lista de Itens Citando | sid.inpe.br/bibdigital/2013/09.24.19.30 1 | |||
| Divulgação | WEBSCI | |||
| Acervo Hospedeiro | sid.inpe.br/mtc-m21b/2013/09.26.14.25.20 | |||
| 6. Notas | ||||
| Campos Vazios | alternatejournal archivingpolicy archivist callnumber copyholder copyright creatorhistory descriptionlevel e-mailaddress format isbn label lineage mark nextedition notes orcid parameterlist parentrepositories previousedition previouslowerunit progress project rightsholder schedulinginformation secondarydate secondarykey session shorttitle sponsor subject tertiarymark tertiarytype url | |||
| 7. Controle da descrição | ||||
| e-Mail (login) | simone | |||
| atualizar | ||||